1121及2206 High heels cotton shoes sole material

Description

  德州市鑫华润科技股份有限公司A/B料产品说明书
    De Zhou Xin HuaRun Technology CO., LTD.
  A/B Shoe Materials Product Manuals

1.特点（Feature） ：女式立跟棉鞋底用料（Polyester polyol for high heels cotton shoes soles）
2.原液特性： Typical properties of PU resin:

品名 Name of products	外观 Appearance (40℃)	粘度 Viscosity (mPa´s/40℃)	密度 Density (g/cm³/40℃)	包装 Package (kg)	保质期 Shelf life (month)	贮存温度 Storage temperature (℃)
HR-P-1121	液状 Liquid	2000±300	1.2±0.02	18 (Net) 蓝标签 Blue label	6	20～25
HR-I-2206	液状或蜡状Liquid or waxy	200±50	1.20±0.02	20 (Net) 黄标签 Yellow label	3	20～25

3.催化剂与辅助剂：Catalyst & Additives:
催化剂HR-C-3的加入量为：250±10g/18kg，水的加入量为：50-80g/18kg
The adding amount of HR-C-3 should be 250±10g/18kg, the adding amount of water should be 50-80g/18kg.
4.成型条件及物性值：Typical processing parameters & Typical Properties:

反应性 Reaction characteristics	技术参数 Technical parameters	项目 Items		物性值 Physical properties
参考配比 A+C/B Mix ratio (By Weight)	100/110-115	成型密度（g/m³） Molded density (g/m³)		0.5-0.6
使用温度（℃） Material Temperature (℃)	38-42/38-42	硬度 Hardness	A型Asker A	85-90
使用温度（℃） Material Temperature (℃)	38-42/38-42	硬度 Hardness	C型Asker C
乳白时间（s） Cream time (s)	4-6	拉伸强度（MPa） Tensile strength (MPa)		≥5.0
升起时间（s） Rise time (s)	30-35	伸长率（%） Elongation (%)		≥400
自由泡密度（g/m³） Free rise foam density (g/m³)	0.25-0.28	撕裂强度（直角）（kN/m） Tear strength (right angle) (kN/m)		≥7.0
金属模具温度（℃） Mold temperature (℃)	45-55	耐折性（零下10℃×10万次） Folding endurance (Minus 10℃×10 million times)		无裂纹
脱模时间（min） Demould time (min)	4-6	DIN耐磨 DIN abrasion resistance		≤200

配合比率是以最佳配比值为基础，此配比值会随添加的颜料助剂种类和添加量不同而变化。The mixing ratio is based on the best proportion, this ratio will be changed with the kind of dye and its adding amount.
自由泡沫密度会依季节（温度，湿度）的不同而变化。Free rise density may vary with temperature & humidity.
该物性数据是对6mm厚的试验片测试获得的数据。These physical data are acquired by testing a sample of 6mm thick.
以上数据仅供参考，具体数据以实际操作为准，如需其他物性指标，请与我公司联系。Data listed above are just for reference. The detail data are subject to practice operation. If other physical properties are required, please contact us.

1109及2209 Cold resistant sole material

1127及2205 Wood-imitation soles material