303 and 2211 Polyester polyol for high resilient sockliner

WeChat

Mobile

The company is mainly engaged in the research, development and production of special functional footwear soles. The products cover special military functional footwear, special environmental footwear, special environmental footwear, and labor insurance shoes. 

Dezhou XinHuaRun Technology Co.,LTD.

©2018 Dezhou Xinhuarun Technology Co., Ltd.   All rights reserved

Company email:

xhrchina@vip.163.com

Company address:

No.28, Shuangyi Road, Decheng District, Dezhou City, Shandong Province

Company phone:

0534-2601366

303 and 2211 Polyester polyol for high resilient sockliner

Description

德州市鑫华润科技股份有限公司A/B料产品说明书
    De Zhou Xin HuaRun Technology CO., LTD.
  A/B Shoe Materials Product Manuals

1.特点(Feature :高回弹鞋垫用料(Polyester polyol for high resilient sockliner

2.原液特性: Typical properties of PU resin:


品名
Name of products

外观
Appearance
(40)

粘度
Viscosity
(mPa´s/40)

密度
Density
(g/cm³/40)

包装
Package
(kg)

保质期
Shelf life
(month)

贮存温度
Storage temperature
()

HR-P-303(POLY)

液状
Liquid

600±200

1.1±0.01

17 (Net)
蓝标签
Blue label

6

20~25

HR-I-2211(ISO)

液状或蜡状Liquid or waxy

300±50

1.20±0.01

20 (Net)
黄标签
Yellow label

3

20~25

3.催化剂与辅助剂Catalyst & Additives:
催化剂HR-C-6的加入量为:250±10g/17kg,水的加入量为:100-140g/18kg
The adding amount of HR-C-6 should be 250±10g/17kg, the adding amount of water should be 100-140g/18kg.
4.成型条件及物性值:Typical processing parameters & Typical Properties:


反应性
Reaction
characteristics

技术参数
Technical
parameters

项目
Items

物性值
Physical
properties

参考配比
A+C/B Mix ratio (By Weight)

100/45-50

成型密度(g/m3)
Molded density (g/m3)

0.25-0.3

使用温度(℃)
Material Temperature (℃)

38-42/38-42

硬度
Hardness

A型Asker A

 

C型Asker C

25-30

乳白时间(s)
Cream time (s)

7-9

拉伸强度(MPa)
Tensile strength (MPa)

≥1.0

升起时间(s)
Rise time (s)

30-35

伸长率(%)
Elongation (%)

≥200

自由泡密度(g/m³)
Free rise foam density (g/m³)

0.13-0.15

耐低温性(零下20℃硬度变化)
Low temperature resistance (Hardness change at minus 20℃)

基本不变

金属模具温度(℃)
Mold temperature (℃)

45-55

压缩歪(%)
Compression ratio (%)

≤10%

脱模时间(min)
Demould time (min)

3-4

回弹率(%)
Resilience ratio (%)

≥35%

  • 配合比率是以最佳配比值为基础,此配比值会随添加的颜料助剂种类和添加量不同而变化。The mixing ratio is based on the best proportion, this ratio will be changed with the kind of dye and its adding amount.
  • 自由泡沫密度会依季节(温度,湿度)的不同而变化。Free rise density may vary with temperature & humidity.
  • 该物性数据是对6mm厚的试验片测试获得的数据。These physical data are acquired by testing a sample of 6mm thick.
  • 以上数据仅供参考,具体数据以实际操作为准,如需其他物性指标,请与我公司联系。Data listed above are just for reference.  The detail data are subject to practice operation. If other physical properties are required, please contact us.