1127及2205 Wood-imitation soles material

WeChat

Mobile

The company is mainly engaged in the research, development and production of special functional footwear soles. The products cover special military functional footwear, special environmental footwear, special environmental footwear, and labor insurance shoes. 

Dezhou XinHuaRun Technology Co.,LTD.

©2018 Dezhou Xinhuarun Technology Co., Ltd.   All rights reserved

Company email:

xhrchina@vip.163.com

Company address:

No.28, Shuangyi Road, Decheng District, Dezhou City, Shandong Province

Company phone:

0534-2601366

1127及2205 Wood-imitation soles material

Description

  德州市鑫华润科技股份有限公司A/B料产品说明书 
    De Zhou Xin HuaRun Technology CO., LTD. 
  A/B Shoe Materials Product Manuals

1.特点(Feature :仿木鞋底用料(Polyester polyol for wood-imitation soles 
2.原液特性: Typical properties of PU resin:


品名 
Name of products

外观 
Appearance
(40)

粘度 
Viscosity
(mPa´s/40)

密度 
Density
(g/cm³/40)

包装 
Package
(kg)

保质期
Shelf life
(month)

贮存温度 
Storage temperature
()

HR-P-1127

液状
Liquid

2500±300

1.2±0.02

18 (Net)
蓝标签
Blue label

6

20~25

HR-I-2205

液状或蜡状Liquid or waxy

200±50

1.20±0.02

20 (Net)
黄标签
Yellow label

3

20~25

3.催化剂与辅助剂Catalyst & Additives:
催化剂HR-C-3的加入量为:250±10g/17kg,水的加入量为:80-110g/18kg
The adding amount of HR-C-3should be 250±10g/17kg, the adding amount of water should be 80-110g/18kg.
4.成型条件及物性值:Typical processing parameters & Typical Properties:


反应性 
Reaction
characteristics

技术参数
Technical
parameters

项目 
Items

物性值 
Physical
properties

参考配比
A+C/B Mix ratio (By Weight)

100/140-150

成型密度(g/m3)
Molded density (g/m3)

0.3-0.35

使用温度(℃)
Material Temperature (℃)

38-42/38-42

硬度
Hardness

A型Asker A

90-95

C型Asker C

 

乳白时间(s)
Cream time (s)

4-6

拉伸强度(MPa)
Tensile strength (MPa)

≥3.0

升起时间(s)
Rise time (s)

30-35

伸长率(%)
Elongation (%)

≥250

自由泡密度(g/m³)
Free rise foam density (g/m³)

0.13-0.15

撕裂强度(直角)(kN/m)
Tear strength (right angle) (kN/m)

≥4.0

金属模具温度(℃)
Mold temperature (℃)

50-65

耐折性(常温25℃×5万次)
Folding endurance (25℃×5 million times)

无裂纹

脱模时间(min)
Demould time (min)

3-4

DIN耐磨
DIN abrasion resistance

≤300

  • 配合比率是以最佳配比值为基础,此配比值会随添加的颜料助剂种类和添加量不同而变化。The mixing ratio is based on the best proportion, this ratio will be changed with the kind of dye and its adding amount.
  • 自由泡沫密度会依季节(温度,湿度)的不同而变化。Free rise density may vary with temperature & humidity.
  • 该物性数据是对6mm厚的试验片测试获得的数据。These physical data are acquired by testing a sample of 6mm thick.
  • 以上数据仅供参考,具体数据以实际操作为准,如需其他物性指标,请与我公司联系。Data listed above are just for reference.  The detail data are subject to practice operation. If other physical properties are required, please contact us.